FV520B Turbine Blade Steel FV520B Forging Parts
Description
FV520B Turbine Blade Steel FV520B Forging Parts is a martensitic precipitation hardening stainless steel which is capable of being hardened by low-temperature treatment. FV520B Turbine Blade Steel FV520B Forging Parts boasts superior corrosion resistance when compared to standard martensitic grades.
All of FV520B Turbine Blade Steel FV520B Forging Parts conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
- Material:Metal,Turbine Blade Steel,FV520B Turbine Blade Steel FV520B Forging Parts
- Shape:Turbine Blade Steel.
- Round bar / Wire rod (Diameter): 5.5mm to 800mm
- Square bar / Flat bar: 3mm to 800mm
- Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
- Heavy/middle plate via hot rolled: T6 - 200mm X W10 - 1500mm X L1000-12000mm
- Sheet steel via cold rolled: T0.5 - 6mm X W6 - 1000mm X L1000 - 2000mm
- Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
- Length: Fixed length or random length or based on the customer's special requirement.
Products Details
FV520B Turbine Blade Steel FV520B Forging Parts
| Chemical Composition (weight%): |
C (％): ≤ 0.070
Si (％): ≤ 0.70
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 13.0 ~ 15.0
Ni (％): 5.00 ~ 6.00
Mo (％): 1.20 ~ 2.00
Cu (％): 1.20 ~ 2.00
Nb + Ta (%): 0.15 ~ 0.60 |
| Mechanical Properties Under Final Heat Treatment: |
Thickness/≤mm: 100
Condition of thermal treatment: AT (Solution treatment)
Hardness ≤HBS: 360
Yield strength σ0.2≥/MPa: -
Tensile strength σb/MPa: ≤1200
Elongation δ ≥(％): -
Elongation δ(transversal )≥(％): -
Impact absorbing power Akv≥/J : -
Condition of thermal treatment: P930
Hardness ≤HBS: -
Yield strength σ0.2≥/MPa: 720
Tensile strength σb/MPa: 930~1100
Elongation δ ≥(％): 15
Impact absorbing power Akv≥/J : 40
Condition of thermal treatment: P1000
Hardness ≤HBS: -
Yield strength σ0.2≥/MPa: 860
Tensile strength σb/MPa: 1000~1200
Elongation δ ≥(％): 10
Impact absorbing power Akv≥/J : -
Condition of thermal treatment: P1070
Hardness ≤HBS: -
Yield strength σ0.2≥/MPa: 1000
Tensile strength σb/MPa: 1070~1270
Elongation δ ≥(％): 10
Impact absorbing power Akv≥/J : - |
Applications:
FV520B Turbine Blade Steel FV520B Forging Parts used most often in the pump shafts, hydraulic equipment used in oil and gas industries, petrochemical, marine and nuclear engineering, and aircraft components such as steam turbine blades.
| Technical Standard | Equivalent Grade |
| ISO/TS 15510(2003) | X6Cr13 |
| JIS G4303(2005) | SUS 405 |
| KS D3706(2006) | STS 405 |
| IS 6527(2001) | X04Cr13 |
| DIN EN 10088-1(2005) | X6Cr13/1.4000 |
| NF EN 10088-2(2005) | X6Cr13 |
| NF A35-573(1984) | Z6CA13 |
| BS 970-1(1996) | 403S17 |
| ASTM A959(2004) | 405/S40500 |
FAQ
Q: How do you control the quality?
A: We have professional inspectors to analyze the chemical composition of raw materials and test the finished products in strict accordance with the standards stipulated in the contract. In this process, the inner and outer surfaces, the appearance of both ends, bending, set length, outer diameter and Wall thickness will be checked one by one. You can rest assured that all products you receive from us are reliable.
Q: Do you accept customization?
A: Yes. If you have special requirements for products or packaging, we can make them for you.
Q: Can you accept trial orders?
A: Our MOQ is usually 1 ton. However, if you want to place an order as the start of our cooperation, we can accept smaller quantities at the first time. Of course, after the start, we will have further and longer cooperation.
Q: How do I get samples?
A: Free samples are available for your inspection and testing, DHL/FedEx/UPS accounts can be used for sampling, and the courier fee is borne by you.